2.5 TAC and the impact of the DCP

TAC both as an organic active agents, but also as a co-crosslinking agent peroxide curing [ 1 ] . This, the author studied the synergistic effect of TAC and DCP , without adding magnesium oxide and accelerators NA-22 , the agent 64 EVA foam manufacturer to the amount of 15 parts by mass changes in performance concrete results in Table 5.

From Table 5 , TAC and DCP content increased , EL showed a downward trend , RL presents no regularity , hardness is not very different appearance to TAC as 1.5 parts , DCP 2.5 to 2.75 parts best . Description In the absence of magnesium oxide and a promoter under the conditions of NA-22 , EVA foam manufacturer agent 64 to 15 parts , the amount of time in order that TAC and DCP speed and EVA foam manufacturer to achieve the best balance of curing rate . Thus also proved less sulfur and sulfur are making the appearance of anomalies over this table 4EVA foam manufacturer and agent 64 is 9 when the results were consistent .

2.6 EVA foam manufacturer agent of

In the basic formulation study EVA foam manufacturer agent 64 on the experimental results of different amounts , see Table 6 . From Table 6 , EVA foam manufacturer to increase the amount of agent 64 , EL increases proportional two persons , with the same mechanism of EVA foam manufacturer . To 16 copies , because of gas evolution is too large, the expansion of the specimen mold , that is not a piece burst . Description In this formula system , EVA foam manufacturer limits the amount of agent 64 to 16 copies.